Resin composition and display unit

ABSTRACT

A display unit that includes an image display part and a light-transmitting protective part arranged on the image display part. A cured resin layer is arranged between the display part and the protective part. The cured resin layer has a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10 7  Pa or less. The cured resin layer is formed from a resin composition that has a cure shrinkage of 5% or less.

This application is a continuation of application Ser. No. 12/308,858 filed Dec. 24, 2008, which is a National Stage of Application of PCT/JP2007/064120 filed Jul. 17, 2007, and claims the benefit of Japanese Application Nos. 2006-193730 and 2007-102251 filed Jul. 14, 2006 and Apr. 9, 2007. The disclosures of the prior applications are hereby incorporated by reference herein in their entirety.

TECHNICAL FIELD

The present invention relates to an image display unit used, for example, in cellular phones. In particular, the invention relates to an image display unit that includes an image display part and a transparent protective part arranged on the image display part, with a cured resin arranged between the image display part and the protective part.

BACKGROUND ART

As this type of display unit, a liquid crystal display unit 101 as shown in FIG. 4 is known. The liquid crystal display unit 101 includes a liquid crystal display panel 102 and a transparent protective part 103 arranged on the liquid crystal display panel 102. The protective part 103 is made of for example, glass or plastic.

To protect the surface of the liquid crystal display panel 102 and a polarizer (not shown), a spacer 104 is arranged between the liquid crystal display panel 102 and the protective part 103 to form a gap 105 between the liquid crystal display panel 102 and the protective part 103.

However, the gap 105 between the liquid crystal display panel 102 and the protective part 103 scatters light, resulting in decreased contrast and luminance of the display unit. The presence of the gap 105 also makes it difficult to design thinner display units.

To address these problems, it has been proposed to fill the gap between the liquid crystal display panel and the protective part with a resin (see, for example, Patent Document 1). However, the stress generated when the resin cures and shrinks causes the deformation of the liquid crystal display panel, resulting in disrupted orientation of the liquid crystal material and other image defects.

-   [Patent Document 1] Japanese Patent Application Laid-Open No.     2005-55641.

DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention

The present invention has been devised in view of the above-described problems associated with prior art. Accordingly, it is an object of the present invention to provide a thin display unit that incorporates a high-luminance, high-contrast image display part that is free of image defects caused by the deformation of the display part.

Means for Solving the Problems

In an effort to achieve the foregoing object, the present inventors drew attention to the fact that the internal stress that builds up within a resin as the resin cures can be approximated by the product of the storage modulus and the cure shrinkage of the cured resin, and found an ideal resin composition for filling the above-described gap between the display part and the protective part of a display unit, that is, a resin composition that shrinks little when cured and has a storage modulus in a suitable range. This finding ultimately led to the present invention.

The present invention devised based on the above-described finding provides an image display unit that includes an image display part, a light-transmitting protective part arranged on the image display part, and a cured resin layer arranged between the image display part and the protective part. The cured resin layer has a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10⁷ Pa or less.

The present invention also provides the cured resin layer arranged between the image display part and the light-transmitting protective part of the image display unit. As described above, the cured resin layer has a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10⁷ Pa or less.

The present invention further provides a resin composition for forming the above-described cured resin layer. The resin composition has a cure shrinkage of 5% or less and its cured resin has a transmittance of 90% or higher in the visible range when formed into a 100 μm-thick layer. The cured resin also has a storage modulus at 25° C. of 1×10⁷ Pa or less.

In the present invention, the image display part may be a liquid crystal display panel.

In the present invention, the protective part may be formed of an acrylic resin.

In the present invention, the protective part may also be formed of an optical glass.

Effect of the Invention

The resin composition of the present invention generates minimum shrinkage stress when it is applied between the image display part and the protective part and cured, so that the effects of the stress on the image display part and the protective part can be minimized. Thus, the image display part and the protective part of the image display unit of the present invention are substantially free of distortion.

Since the cured product of the resin composition of the present invention, namely the cured resin, has a refractive index closer to that of the panels used to make the image display part and the protective part, than does the gap between the liquid crystal display panel and the protective part, light reflection is suppressed at the interface between the protective part and the cured resin or at the interface between the cured resin and the image display part.

As a result, the image display unit of the present invention achieves high-luminance, high-contrast display of images without causing any image defects.

The image display unit of the present invention can effectively prevent the disrupted orientation of liquid crystal materials and other image defects and can therefore achieve high-quality display of images especially when the image display part is a liquid crystal display panel.

Furthermore, the presence of the cured resin between the image display part and the protective part reinforces the image display unit of the present invention, making it resistant to high impacts.

In addition, the present invention can provide image display units that are thinner than any of the conventional image display units that have a gap between the image display part and the protective part.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view showing essential components of one embodiment of display unit according to the present invention.

FIG. 2 is a cross-sectional view showing essential components of another embodiment of display unit according to the present invention.

FIG. 3 is a cross-sectional view showing essential components of still another embodiment of display unit according to the present invention.

FIG. 4 is a cross-sectional view showing essential components of a conventional display unit.

DESCRIPTION OF REFERENCE NUMERALS

-   1, 1B display unit -   2 display part -   3 protective part -   4 spacer -   5 cured resin or cured resin layer -   6, 7 polarizer

BEST MODE FOR CARRYING OUT THE INVENTION

Preferred embodiments of the present invention will now be described with reference to the accompanying drawings, in which the same numerals denote the same or similar elements.

FIGS. 1 and 2 are cross-sectional views each showing one embodiment of display unit according to the present invention.

With reference to FIG. 1, a display unit 1 of the present embodiment includes a display part 2 that is connected to a drive circuit (not shown) and displays predetermined images, and a light-transmitting protective part 3 that is arranged in the vicinity of the display part 2 and faces the display part 2.

In the display unit 1 of the present embodiment, the display part 2 is a liquid crystal display panel used in a liquid display apparatus.

The liquid crystal display apparatus is not limited to a particular type, but can be applied to various systems. Examples of such liquid crystal display apparatuses include those for use in cellular phones, portable game machines and other electronic devices.

When the display part 2 is a liquid crystal display panel, polarizers 6, 7 are arranged on each side of the display part 2 as shown in FIG. 2.

The protective part 3 is formed of a planar member having substantially the same size as the display part 2. The protective part 3 is preferably formed of an optical glass or plastic (such as an acrylic resin).

The protective part 3 is spaced apart from the display part 2 by a spacer 4 arranged along the periphery of the display part 2. The thickness of the spacer is about in the range of from 0.05 mm to 1.5 mm and serves to keep the distance between the surfaces of the display part 2 and the protective part 3 at approximately 1 mm.

The display unit 1 includes a cured resin layer 5 provided between the display part 2 and the protective part 3.

In the present invention, the cured resin layer 5 has a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1.0×10⁷ Pa or less, and preferably from 1.0×10³ to 1.0×10⁶ Pa. The resin composition to make the cured resin layer 5 has a cure shrinkage of 5% or less, preferably 4.5% or less, and more preferably from 0 to 2%.

The image display unit of the present invention is preferably configured without using the spacer 4 used in the above-described embodiments of the display unit 1 shown in FIGS. 1 and 2. Specifically, the resin composition layer 5 and the protective part 3 are sequentially overlaid on the display part 2. Curing the resin composition completes an image display unit 1B as shown in FIG. 3 without providing the spacer. In this configuration, the distance between the display part 2 and the protective part 3 (thus, the thickness of the cured resins layer 5), which is determined by factors such as viscosity and density of the resin composition and weight of the protective part 3, is typically in the range of from 50 μm to 200 μm. Such a configuration therefore makes it possible to design thinner image display units.

In the present invention, the resin composition to make the cured resin layer 5 is preferably a photocurable resin composition in order to increase the productivity, although other resins may also be used.

The resin composition for use in the present invention preferably contains at least one polymer, such as polyurethane acrylates, polyisoprene acrylates and esters thereof, hydrogenated terpene resins or butadiene polymers; at least one acrylate monomer, such as isobornyl acrylate, dicyclopentenyloxyethyl methacrylate or 2-hydroxybutyl methacrylate; and at least one photopolymerization initiator, such as 1-hydroxy-cyclohexyl-phenyl-ketone.

Since the protective part 3 often has a UV-cutting function to protect the display part 2 against ultraviolet rays, the photopolymerization initiator for use in the present invention is preferably used together with a photopolymerization initiator that can cure in the visible range (such as SpeedCure TPO (trade name), Nihon Siber Hegner KK).

The resin composition for use in the present invention is prepared such that the cured resin obtained by curing the resin composition by UV irradiation has a storage modulus (at 25° C.) of 1×10⁷ Pa or less, and preferably in the range of from 1×10³ Pa to 1×10⁶ Pa, has a refractive index preferably in the range of from 1.45 to 1.55, and more preferably in the range of from 1.51 to 1.52, and has a transmittance of 90% or higher in the visible range when formed into a 100 μm-thick layer. Different resin compositions containing the same major resin component but different auxiliary resin components and monomer components may be cured to have different storage moduli (at 25° C.) that may, in some cases, exceed 1×10⁷ Pa. Those resin compositions that are cured to have a storage modulus (at 25° C.) of higher than 1×10⁷ Pa are not included in the scope of the present invention.

The resin composition of the present invention also has a preferable cure shrinkage of 5% or less, more preferably of 4.5% or less, and still more preferably in the range of from 0 to 2%. In this manner, the internal stress that builds up within the cured resin upon curing of the resin composition can be reduced, and the distortion generated at the interface between the cured resin layer 5 and the display part 2 or the protective part 3 can be prevented.

Thus, by arranging the resin composition between the display part 2 and the protective part 3 and then curing the resin composition, the amount of light scattered at the interface between the cured resin layer 5 and the display part 2 or the protective part 3 can be reduced. As a result, the luminance and the visibility of the displayed images can be improved.

The magnitude of the internal stress that builds up within the cured resin upon curing of the resin composition can be evaluated by dropping the resin composition onto a flat surface and measuring the average surface roughness of the cured resin. In practice, the distortion generated at the interface between the display part 2 or the protective part 3 and the cured resin arranged in between would be negligible if, for example, a cured resin obtained by dropping 2 mg of the resin composition onto a glass plate and cured by UV irradiation to 90% or a higher cure ratio has an average surface roughness of 6 nm or less. By using the resin composition of the present invention, this average surface roughness can be kept at 6 nm or less, and preferably in the range of 1 nm to 3 nm.

To fabricate the display unit 1 of the present invention, the spacer 4 and a ridge (not shown) are arranged on the display part 2 along its periphery. A predetermined amount of the above-described photocurable resin composition is then poured over the display member 2 in the area inside the spacer and the ridge.

The protective part 3 is then placed on the display part 2 over the spacer 4 and the gap between the display part 2 and the protective part 3 is completely filled with the resin composition.

Subsequently, the resin composition is irradiated with ultraviolet rays via the protective part 3 to cure the resin composition. This completes the desired display unit 1.

When it is desired to fabricate the display unit 1B in which the spacer 4 is omitted, the above-described photocurable resin composition is first applied onto the display part 2. The protective part 3 is then placed over the coating of the resin composition and the ultraviolet rays are irradiated onto the resin composition from the side of the protective part 3.

In the image display units 1, 1B of the present invention obtained in the foregoing manner, the effects of the stress generated as the resin cures and shrinks on the display part 2 and the protective part 3 can be minimized, so that little or no distortion is generated in the display part 2 and the protective part 3. Since the display part 2 is not deformed during the production, it can display images at high luminance and high contrast without causing any image defects.

In addition, the cured resin 5 that fills the gap between the display part 2 and the protective part 3 in the present embodiment reinforces the display unit 1 so that it can withstand high impacts. This makes it possible to design thinner display units 1.

In particular, when the image display part 2 is a liquid crystal display panel, the present invention can provide a liquid crystal display apparatus that can effectively prevent disrupted orientation of liquid crystal materials and other image defects and can thus achieve high-quality display of images especially.

While the present invention is suitable for use in the above-described liquid crystal display apparatuses, the invention is also applicable to various other panel displays, such as organic EL apparatuses and plasma display apparatuses.

EXAMPLES

The present invention will now be described in detail with reference to Examples and Comparative Examples, which are not intended to limit the scope of the invention in any way.

Example 1

The following components were kneaded together in a kneader to make a resin composition of Example 1: 50 parts by weight of polyurethane acrylate, 30 parts by weight of isobornyl acrylate, 3 parts by weight of a photopolymerization initiator and 1 part by weight of a photopolymerization initiator for visible-range.

Example 2

The following components were kneaded together in a kneader to make a resin composition of Example 2: 70 parts by weight of an ester formed from a maleic anhydride adduct of a polyisoprene polymer and 2-hydroxyethyl methacrylate, 30 parts by weight of dicyclopentenyloxyethyl methacrylate, 10 parts by weight of 2-hydroxybutyl methacrylate, 30 parts by weight of a hydrogenated terpene resin, 140 parts by weight of a butadiene polymer, 4 parts by weight of a photopolymerization initiator and 0.5 parts by weight of a visible-range photopolymerization initiator.

Example 3

The following components were kneaded together in a kneader to make a resin composition of Example 3: 100 parts by weight of an ester formed from a maleic anhydride adduct of a polyisoprene polymer and 2-hydroxyethyl methacrylate, 30 parts by weight of dicyclopentenyloxyethyl methacrylate, 10 parts by weight of 2-hydroxybutyl methacrylate, 30 parts by weight of a hydrogenated terpene resin, 210 parts by weight of a butadiene polymer, 7 parts by weight of a photopolymerization initiator and 1.5 parts by weight of a visible-range photopolymerization initiator.

Comparative Example 1

The following components were kneaded together in a kneader to make a resin composition of Comparative Example 1: 50 parts by weight of polybutadiene acrylate, 20 parts by weight of hydroxyethyl methacrylate, 3 parts by weight of a photopolymerization initiator and 1 part by weight of a visible-range photopolymerization initiator.

Comparative Example 2

The following components were kneaded together in a kneader to make a resin composition of Comparative Example 2: 50 parts by weight of polyurethane acrylate, 30 parts by weight of tricyclodecane dimethanol acrylate, 3 parts by weight of a photopolymerization initiator and 1 part by weight of a visible-range photopolymerization initiator.

Comparative Example 3

The following components were kneaded together in a kneader to make a resin composition of Comparative Example 3: 50 parts by weight of polybutadiene acrylate, 20 parts by weight of isobornyl acrylate, 3 parts by weight of a photopolymerization initiator and 1 part by weight of a visible-range photopolymerization initiator.

Evaluation 1

Each of the resin compositions prepared in Examples 1 through 3 and Comparative Examples 1 through 3 was poured onto a 100 μm-thick white glass plate to a predetermined thickness. The plates were transported on a UV-conveyor to obtain cured resins having a predetermined thickness. The cured resins were used as samples.

The light transmittance, elastic modulus, cure shrinkage and surface roughness of each sample were determined as described below.

[Light Transmittance]

Using a UV-Visible spectrophotometer (V-560, Jasco Corp.), each sample (with 100 μm-thick cured resin) was analyzed for the transmittance in the visible range. It turned out that all of the samples had 90% or a higher transmittance.

[Elastic Modulus]

Using a viscoelastometer (DMS6100, Seiko Instruments Inc.), the elastic modulus (at 25° C.) of each sample (with 2 mm-thick cured resin) was measured at a frequency of 1 Hz.

[Cure Shrinkage]

The cure shrinkage of each sample was determined by the following equation using the difference in the specific gravity between the uncured resin solution and the cured solid product, as measured by an electronic specific gravity meter (SD-120L, Mirage Co.). cure shrinkage (%)={(specific gravity of cured resin−specific gravity of resin solution)/(specific gravity of cured resin)}×100 [Surface Roughness]

Using a three-dimensional non-contact surface roughness meter (Zygo Corp.), each sample (with 1 mm-thick cured resin) was analyzed for the distortion (Ra: average surface roughness) in a predetermined area (2.93 mm×2.20 mm) of the glass plate surface caused by the internal stress generated during UV curing.

These results are shown in Table 1.

TABLE 1 Properties of Examples and Comparative Examples and corresponding evaluation results Elastic modulus Cure shrinkage Ra: average surface (Pa) (%) roughness (nm) Example 1 1 × 10⁶ 4.5 5.5 Example 2 1 × 10⁴ 1.8 2.7 Example 3 4 × 10³ 1.0 1.5 Comparative 2 × 10⁷ 5.6 12.4 Example 1 Comparative 3 × 10⁸ 4.3 36.5 Example 2 Comparative 5 × 10⁸ 5.6 64.2 Example 3

As can be seen from Table 1, the average surface roughness Ra was from 1.5 nm to 5.5 nm in each of Examples 1 through 3, indicating that samples in these Examples were each distorted little.

In comparison, Ra was significantly large in each of Comparative Example 1 (Ra=12.4 nm), Comparative Example 2 (Ra=36.5 nm) and Comparative Example 3 (Ra=64.2 nm), suggesting that the internal stress generated upon curing of the resin in each of Comparative Examples 1 through 3 caused distortion at the interface between the resin and the glass plate.

Evaluation 2 [Impact Resistance]

The resin composition of Example 1 was cured between a 50 mm×50 mm×0.5 mm glass plate (display part) and a 50 mm×50 mm×0.5 mm polycarbonate plate (protective part) to form a 0.1 mm-thick layer between the two plates. The resulting panel served as the sample panel of Example. In this configuration, the spacer was omitted and the sample panel had a total thickness of 1.1 mm. To fabricate the sample panel, the resin composition of Example 1 was first applied to the glass plate and the polycarbonate plate was placed over the coating of the resin composition. The resin composition was then cured by the irradiation of UV from the side of the polycarbonate plate.

Meanwhile, a sample panel having the conventional configuration as shown in FIG. 4 was prepared. The liquid crystal display panel (display part) 102 and the protective part 103 used were identical to those used to make the sample panel of Example. The display part and the protective part were assembled with 1.0 mm thick spacers arranged in between to make the sample panel of Comparative Example having a 1.0 mm air gap and a total thickness of 2.0 mm.

Each of the sample panels of Example and Comparative Example was secured to a mount by the periphery using a predetermined jig. A panel breakage test was then performed by perpendicularly pressing a press member, 5 mm in diameter, against the surface of the protective part at a press speed of 1 mm/sec.

The sample panel of Comparative Example with the air gap formed between the display part and the protective part broke at 1 N/cm², whereas the sample panel of the present invention broke at 1.43 N/cm².

The results demonstrate that the panel of Example has a press strength that is 43% higher than that of the panel of Comparative Example, yet has a decreased thickness as compared to the panel of Comparative Example. 

The invention claimed is:
 1. A method of producing an image display unit comprising an image display part, a transparent protective part arranged on the image display part, and a cured resin layer arranged between the image display part and the protective part, the method comprising: a step of completely filling a gap between the image display part and the transparent protective part with a resin composition including a photo polymerization initiator that can cure in the visible and ultraviolet ranges, and a step of forming the cured resin layer by irradiating the resin composition with ultraviolet rays from the protective part; wherein the cured resin layer has: (a) a cure ratio of 90% or more; (b) a cure shrinkage in a range of from 0 to 2% and a storage modulus at 25° C. of 4.0×10³ to 1.0×10⁶, where these cure shrinkage and storage modulus values are achieved while the cure ratio becomes 90% or more so as to suppress effects of an internal stress that builds up within the resin composition as the resin composition cures and can be approximated by the product of the storage modulus and the cure shrinkage of the cured resin; and (c) a transmittance of 90% or more in the visible range.
 2. The method according to claim 1, wherein the cured resin layer has a thickness of 50 to 200 μm.
 3. The method according to claim 1, wherein the image display part is a liquid crystal display panel.
 4. The method according to claim 1, wherein the protective part is formed of an acrylic resin.
 5. The method according to claim 1, wherein the protective part is formed of glass.
 6. The method according to claim 1, wherein the resin composition further comprises at least one polymer, and at least one acrylate monomer.
 7. The method according to claim 1, wherein the resin composition comprises: at least one polymer selected from the group consisting of polyurethane acrylates, polyisoprene acrylates and esters thereof, hydrogenated terpene resins, and butadiene polymers; at least one acrylate monomer selected from the group consisting of isobornyl acrylate, dicyclopentenyloxyethyl methacrylate, and 2-hydroxybutyl methacrylate; and the photopolymerization initiator.
 8. The method according to claim 1, wherein the polymer includes a butadiene polymer. 